    2. 生物質顆粒機是如何成型的,不理想的緣由是什么?

      來源:http://www.fruof.icu 發布時間:2019-07-03 瀏覽次數:
        生物質顆粒機成型不好很多用戶整天用研磨工具來研究,不知道生物質顆粒機成型的影響有很多原因,工程師先帶您了解一下生物質顆粒機成型是如何進行的:
        The biomass granulator is not well formed. Many users use grinding tools to study it all day. They don't know the impact of biomass granulator forming for many reasons. The engineer will first show you how the biomass granulator forming is carried out.
        根據生物質制粒機的成型機理,生物質木質素可以連接在一起的基本條件是要有合適的成型溫度。一方面,提高溫度可以使原料中木質素軟化;另一方面,它可以使原材料本身柔軟,易于壓縮。在自然含水率條件下,木質素軟化點溫度為80 ~ 130℃。當加熱到70 ~ 100℃時,木質素的粘合力開始增加,當溫度達到160 ~ 250℃時,木質素可以熔化。因此,生物質成型時的加熱溫度不應低于軟化點溫度。加熱溫度不僅影響原料成型,而且影響生物質顆粒機的工作效率,加熱溫度應調整到一定范圍。
        According to the forming mechanism of biomass granulator, the basic condition for biomass lignin to be joined together is the appropriate forming temperature. On the one hand, increasing the temperature can soften the lignin in the raw material; on the other hand, it can make the raw material itself soft and easy to compress. Under the condition of natural water content, the softening point temperature of lignin is 80 - 130 C. When heated to 70 - 100 C, the adhesion of lignin begins to increase, and when the temperature reaches 160 - 250 C, lignin can melt. Therefore, the heating temperature of biomass shaping should not be lower than the softening point temperature. Heating temperature not only affects the raw material forming, but also affects the working efficiency of biomass granulator. Heating temperature should be adjusted to a certain range.
      生物質顆粒機生產廠家
        生物質顆粒機是如何成型的,不理想的緣由是什么?-生物質顆粒機生產廠家:http://www.fruof.icu
        How is the biomass granulator formed and why is it not ideal? - Biomass granulator manufacturer: http://www.fruof.icu
        溫度過低,不僅原料不能成型,而且能耗增加;隨著溫度的升高,電機的功耗降低,但成型壓力降低,成型材料壓制不當,密度降低,易斷裂損壞,顆粒表面過熱燒焦,煙氣較大。
        When the temperature is too low, not only the raw material can not be formed, but also the energy consumption increases. With the increase of temperature, the power consumption of the motor decreases, but the forming pressure decreases, the forming material is improperly pressed, the density decreases, and it is easy to break and damage. The surface of the particles is overheated and charred, and the smoke is larger.
        雖然龍騰生物質顆粒機沒有外部熱源加熱,但在成型過程中,原料與機器部件之間的摩擦也可以將原料加熱到100℃,同樣可以使原料木質素軟化,起到粘結劑的作用。最后的形狀是冷卻后形成的。
        Although Longteng biomass granulator has no external heat source to heat, the friction between raw materials and machine parts can also heat the raw materials to 100 C, which can also soften the lignin of raw materials and act as a binder. The final shape is formed after cooling.
        生物質顆粒機是如何成型的,不理想的緣由是什么?-生物質顆粒機生產廠家:http://www.fruof.icu
        How is the biomass granulator formed and why is it not ideal? - Biomass granulator manufacturer: http://www.fruof.icu
        當然,上述條件都是在生物質原料強度、壓力輥、磨料壓縮比、進料量、原料含水量等諸多因素處于理想狀態下。
        Of course, the above conditions are in the ideal state for the strength of biomass raw materials, pressure rolls, abrasive compression ratio, feed volume, water content of raw materials and many other factors.
        因此,以生物質顆粒成型必須以以上幾點為前提,對解決生物質顆粒機成型問題不佳的原因需要一一列舉。龍騰工程師會根據現場生產情況為您找到準確的原因。想要了解更多內容,歡迎訪問生物質顆粒機生產廠家網站:http://www.fruof.icu
        Therefore, in order to solve the problem of biomass granulation, the precondition of biomass granulation must be the above points, and the reasons for the poor formation of biomass granulator need to be enumerated. Longteng Engineer will find out the exact reason for you according to the on-site production situation. For more information, please visit the biomass granulator manufacturer's website: http://www.fruof.icu